%J Constant Elastic Characterization of Isotropic Materials through Electronic Optical Holography combined to the Mechanical Resonance Method
%@secondarytype TAE
%X Nesta dissertação apresenta-se uma técnica para medir constantes elásticas de materiais isotrópicos é estudada e analisada. A geometria, massa e freqüências de ressonância (na flexão e na torção dinâmica), de uma viga de seção transversal retangular, são usadas para determinar as característica elásticas de materiais isotrópicos pela norma ASTM C1198-91. Através da medição de amplitude de vibração da superfície da viga no primeiro modo de ressonância à flexão, pode-se caracterizar as mesmas propriedades elásticas do material, obtendo-se o módulo de elasticidade da mesma forma recomendada pela norma e o coeficiente de Poisson, através de imagens obtidas por holografia óptica eletrônica  ESPI (Electronic Speckle Pattern Interferometry), com iluminação estroboscópica. Um mapa de franjas associado ao campo de deslocamento é medido onde, através de processamento digital da imagem extraem-se informações para a quantificação do coeficiente de Poisson. Estes dados são analisados por um modelo matemático implementado através de três diferentes algoritmos, baseados na equação dada por Timoshenko que descreve o campo de deslocamentos fora do plano de uma viga sob flexão pura . Embora sendo um modelo para vigas submetidas à flexão pura na condição estática, mostra-se eficiente para determinar o coeficiente de Poisson na condição dinâmica. Para estimar a incerteza trazida por influências na sintonia da freqüência de ressonância, posicionamento dos apoios da barra durante a vibração e espessura do objeto, vários ensaios repetitivos foram realizados. Diferentes corpos de provas e diferentes materiais foram ensaiados, primeiramente utilizando-se do procedimento recomendado pela norma e posteriormente pelo procedimento proposto neste trabalho. O procedimento descrito na norma foi utilizado como referência para comparação dos resultados obtidos pela técnica estudada. ABSTRACT: Several techniques have been used to measure elastic constants of isotropic materials. The ASTM C1198-91 standard can be used for determining both the Young modulus and Poissons ratio. The geometry, mass and resonance frequencies (flexural and torsional) of a beam with rectangular cross section have to be accurately measured in order to determine this elastics parameters. An alternative technique to measure elastic constants of isotropic materials is discussed and analyzed in this master dissertation. The vibration amplitude field of the beam in the first flexural resonance mode is measured using ESPI  Electronic Speckle Pattern Interferometry  with stroboscopic illumination. In order to determine the Poissons ratio a fringes map associated to the displacement field is measured through the digital processing of the image. The static model for pure bending (Timoshenko solution) is fitted to the measured data through three different algorithms. This model is shown efficient to determine the Poissons ratio in the dynamic condition. Some factors like frequency tuning of the resonance frequency, the positioning of the supporting points of the beam during vibration and the thickness of the specimen have some influences on the results accuracy and are investigated. In order to do it, several measurement test were repeated for different specimens with different materials and geometry. The values obtained through the ASTM C1198-91 standard were used as reference to estimate the overall accuracy of the developed technique.
%@secondarydate 2005-12-01
%T Caracterização de constantes elásticas de materiais isotrópicos por holografia óptica eletrônica combinada ao método de ressonância mecânica
%I Instituto Nacional de Pesquisas Espaciais
%K Holografia, materiais, propriedades elásticas, vibrações, ressonância, ensaios mecânicos, medidas ópticas, holography, materials, elastics properties, vibration, resonance, mechanical tests, optics measurements.
%P 132
%8 1998-12-23
%C São José dos Campos
%@copyholder SID/SCD
%@secondarykey INPE-13262-TAE/62
%E Gonçalves Jr., Armando Albertazzi,   (orientador),
%E Schneider, Carlos Alberto,
%E Cavaco, Marco Antônio Martins,
%E Bernardini, Pedro A. Nannetti,
%2 sid.inpe.br/MTC-m13@80/2006/07.12.14.47.46
%4 sid.inpe.br/MTC-m13@80/2006/07.12.14.47
%9 Trabalhos Acadêmicos Externos
%D 2005
%Y Gonçalves Jr., Armando Albertazzi,
%A Sutério, Ricardo,