| 1. Identificação | |
| Tipo de Referência | Artigo em Revista Científica (Journal Article) |
| Site | mtc-m16b.sid.inpe.br |
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
| Identificador | 6qtX3pFwXQZGivnK2Y/S9j6Q |
| Repositório | sid.inpe.br/mtc-m17@80/2007/11.13.13.02 (acesso restrito) |
| Última Atualização | 2007:11.13.13.02.41 (UTC) administrator |
| Repositório de Metadados | sid.inpe.br/mtc-m17@80/2007/11.13.13.02.43 |
| Última Atualização dos Metadados | 2018:06.05.03.35.01 (UTC) administrator |
| Chave Secundária | INPE-14900-PRE/9814 |
| ISSN | 0257-8972 |
| Chave de Citação | SilvaUedaNaka:2007:EnCoRe |
| Título | Enhanced corrosion resistance of AISI H13 steel treated by nitrogen plasma immersion ion implantation  |
| Ano | 2007 |
| Mês | Aug. |
| Data de Acesso | 30 abr. 2024 |
| Tipo Secundário | PRE PI |
| Número de Arquivos | 1 |
| Tamanho | 381 KiB |
| 2. Contextualização | |
| Autor | 1 Silva, Leide Lili Gonçalves da 2 Ueda, Mário 3 Nakazato, R. Z. |
| Grupo | 1 LAP-INPE-MCT-BR 2 LAP-INPE-MCT-BR |
| Afiliação | 1 Instituto Nacional de Pesquisas Espaciais (INPE) 2 Instituto Nacional de Pesquisas Espaciais (INPE) 3 Faculdade de Engenharia de Guaratinguetá. Universidade Estadual Paulista (FEG.UNESP) |
| Endereço de e-Mail do Autor | 1 leide@plasma.inpe.br |
| Revista | Surface and Coatings Technology |
| Volume | 2001 |
| Número | 19/20 |
| Páginas | 8291-8294 |
| Histórico (UTC) | 2007-11-13 13:02:43 :: simone -> administrator :: 2012-10-25 03:23:05 :: administrator -> simone :: 2007 2013-02-20 15:20:02 :: simone -> administrator :: 2007 2018-06-05 03:35:01 :: administrator -> marciana :: 2007 |
| 3. Conteúdo e estrutura | |
| É a matriz ou uma cópia? | é a matriz |
| Estágio do Conteúdo | concluido |
| Transferível | 1 |
| Tipo do Conteúdo | External Contribution |
| Palavras-Chave | AISI H13 steel plasma immersion ion implantation hardness corrosion nitride layer INDUSTRIAL COMPONENTS |
| Resumo | Electrochemical corrosion measurements of AISI H13 steel treated by Pill process in 3.5% (wt) NaCl solution were investigated. So far the corrosion behavior of AISI H 13 steel by Pill has not been studied. The electrochemical results are correlated with the surface morphology, nitrogen content and hardness of the nitride layer. Ion implantation of nitrogen into H 13 steel was carried out by Pill technique. SEM examination revealed a generalized corrosion and porosity over all analyzed sample surfaces. Penetration of nitrogen reaching more than 20 gm was achieved at 450 degrees C and hardness as high as 1340 HV (factor of 2.7 enhancement over standard tempered and annealed H 13) was reached by a high power, 9 h Pill treatment. The corrosion behavior of the samples was studied by potentiodynamic polarization method. The noblest corrosion behavior was observed for the samples treated by PIII at 450 degrees C, during 9 h. Anodic branches of polarization curves of PIII processed samples show a passive region associated with the formation of a protective film. The passive region current density of PIII treated H13 samples (3.5 x 10(-6) A/cm(2)) is about 270 times lower than the one of untreated specimens, which demonstrates the higher corrosion resistance for the Pill treated H 13 samples. |
| Área | FISPLASMA |
| Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAP > Enhanced corrosion resistance... |
| Conteúdo da Pasta doc | acessar |
| Conteúdo da Pasta source | não têm arquivos |
| Conteúdo da Pasta agreement | não têm arquivos |
| 4. Condições de acesso e uso | |
| Idioma | en |
| Arquivo Alvo | enhanced corrosion resistance.pdf |
| Grupo de Usuários | administrator simone |
| Visibilidade | shown |
| Detentor da Cópia | SID/SCD |
| Política de Arquivamento | denypublisher denyfinaldraft24 |
| Permissão de Leitura | deny from all and allow from 150.163 |
| 5. Fontes relacionadas | |
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ET2RFS |
| Divulgação | WEBSCI; PORTALCAPES. |
| Acervo Hospedeiro | lcp.inpe.br/ignes/2004/02.12.18.39 cptec.inpe.br/walmeida/2003/04.25.17.12 |
| 6. Notas | |
| Campos Vazios | alternatejournal archivist callnumber copyright creatorhistory descriptionlevel documentstage doi e-mailaddress format isbn label lineage mark mirrorrepository nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress project readergroup resumeid rightsholder schedulinginformation secondarydate secondarymark session shorttitle sponsor subject tertiarymark tertiarytype typeofwork url versiontype |
| 7. Controle da descrição | |
| e-Mail (login) | marciana |
| atualizar | |